Slip On flange
The calculated strength from a Slip On flange under internal pressure is of the order of two-thirds that of Welding Neck flanges, and their life under fatigue is about one-third that of the latter.
The connection with the pipe is done with 2 fillet welds, as well at the outside as also at the inside of the flange.
The X measure on the image, are approximately:
Wall thickness of pipe + 3 mm.
This space is necessary, to do not damage the flange face, during the welding process.
A disadvantage of the flange is, that principle always firstly a pipe must be welded and then just a fitting. A combination of flange and elbow or flange and tee is not possible, because named fittings have not a straight end, that complete slid in the Slip On flange.
Materials Carbon Steel: ASTM A105. ASTM A350 LF1. LF2, CL1/CL2, A234, S235JRG2, P245GH P250GH, P280GHM 16MN, 20MN ,20# Stainless Steel: ASTM A182, F304/304L, F316/316L Types Slip On Plate Flange/Plate Flange , Slip On Hub Flange/Bossed Welding Neck Flange/WN flange/ Loose Flange/Lapped Flange /Backing Flange Blind Flange/Blank flange, Lap Joint Flange /LJ Flange Socket Weld Flange/SW Flange Threaded Flange/Screwed Flange Loose Flange/Lapped Flange Backing Flange RTJ /o-Ring Custom Flange/Special Flange Hot/Cold/Electro Gavanized Flange Standards ANSI/ASME/ASA B16.5 FLANGES, ANSI B16.47 A/B FLANGES JIS B 2220 FLANGES, KS B 1503, DIN SERIES, UNI, EN1092-1, BS4504 BS 10 TABLE D/E/F FLANGES, SANS 1123 FLANGES/SABS 1123 GOST12820-80/GOST12821-80, NFE29203/NS/AS/ISO/AWWA FLANGES Pressure &Ratings 150LBS, 300,600,900,1500,2500 ANSI, ASA B16.5 PN6 PN10 PN16 PN25 PN40 PN64-DIN/UNI PN6 PN10 PN16 PN25 PN40 PN63-EN1092-1/BS4504 PN0.6Pa, PN1.0Pa, PN1.6. PN2.5,PN4.0-GOST12820-80 PN0.6Pa, PN1.0Pa, PN1.6. PN2.5,PN4.0, PN6.3. -GOST12821-80 600kPa, 1000.1600.2500.4000.-SANS 1123 5KG, 10KG, 16KG, 20KG, 30KG, 40KG-JIS B2220/KS B1503 TABLE D, TABLE E ,TABLE F-BS 10, AS2129 CLASS D, CLASS E, CALSS F, AWWA C207 Surface Treatment Rust Prevention , Black Paint Coating or Phosphating Treatment with Black Color Varnish Paint Coating, Varnish Oil Coating, Electro Galvanizing Coating (Cold Galvanizing, Color Golden or silvery white, Coating thickness 20~30(um) Hot Dip Galvanizing Coating (Coating Thickness 200um around) Technical Forging Application Water works, Shipbuilding industry, Petrochemical & Gas industry, Power industry, Valve industry and general pipes connecting projects etc. Inspection Quality Control System-Well Equipments and Machinery-Well Workers and Engineers Packing Wooden Pallets or Wooden Cases or As Customers' Requirements Payment Terms L/C Or 30 % Advance By T/T and The balance Will be Paid After the copy of B/L Delivery Time 30 Days \after the Advance or the L/C After-Sales Service Orders and Products Tracking System