Hastelloy B-2,UNS Number N010665 pipes

CONSULTATION SEND E-MAIL
  • Hastelloy B-2,UNS Number N010665 pipes

Product Information

 
Hastelloy B-2,UNS Number N010665 pipes
Hastelloy B Chemical compostion:
Alloy
%
Ni
Mo
Fe
Cr
Co
C
Mn
V
Si
P
S
Hastelloy B
Min.
Balance
26
4.0
 
 
 
 
0.2
 
 
 
Max.
30
6.0
1.0
2.5
0.05
1.0
0.4
1.0
0.04
0.03
Hastelloy B-2
Min.
Balance
26
2.0
 
 
 
 
 
 
 
 
Max.
30
7.0
1.0
1.0
0.02
1.0
 
0.1
0.04
0.03

 
Hastelloy B Physical properties:

 

Density
9.24g/cm3
Melting point
1330-1380°C

 

 

Hastelloy B Alloy minimum mechanical properties in the room temperature:

 

Alloy state
Tensile strength
Rm N/mm2
Yield strength
RP0.2N/mm2
Elongation
A5 %
Hastelloy B
690
310
40

 

Characteristic:
1. Control of iron and chromium content to a minimum to prevent the generation of β-phase Ni4Mo.
2. Excellent corrosion resistance of restore environment.
3. An excellent resist to concentration sulfuric acid medium and large number of non-oxidizing acid corrosion.
4. A very good resistance of chloride reduction of stress corrosion cracking (SCC).
5. Good corrosion resistance of various organic acids.

Metallurgical structure
Hastelloy B-2 is the face-centered cubic lattice structure. By controlling the content of iron and chromium at the minimum to reduce the processing brittle, prevent Ni4Mo precipitation during 700-870 °C.

Corrosion resistance
Ni-Mo alloy Hastelloy B-2, the carbon and silicon content is extremely low, reducing the HAZ carbon and other impurities precipitation, so the weld has sufficient corrosion resistance. Alloy Hastelloy B-2 in the reduction of medium with very good corrosion resistance, such as a various temperature and concentration of hydrochloric acid. In the middle of the concentration of sulfuric acid solution (or contain a certain amount of chloride ions) also has very good corrosion resistance. At the same time can be used to acetic acid and phosphoric acid environment. Alloy material suitable only in the metallurgical structure and pure crystal structure in order to have the best corrosion resistance.

Applied field:
Alloy Hastelloy B-2 with a wide range of applications in the field of chemical, petrochemical, energy manufacturing and pollution control , particularly in the sulfuric acid, hydrochloric acid, phosphoric acid, acetic acid, and other industries.