Nickel Alloy Steel Pipe

Your position: Home > Products > Stainless Steel Pipes > Nickel Alloy Steel Pipe > Nickel Alloy Pipes Incoloy 901 (UNS N09901/Din 1.4898)

Nickel Alloy Pipes Incoloy 901 (UNS N09901/Din 1.4898)

CONSULTATION SEND E-MAIL

Product Information

Nickel Alloy Pipes Incoloy 901 (UNS N09901/Din 1.4898)

Incoloy 901 Chemical composition:

Alloy	%	Ni	Cu	Al	Fe	Ti	Co	Mn	S	C	Si	P	Cr	Mo	B
Incoloy 901	Min.	40.0				2.35							11.0	5.0	0.01
Incoloy 901	Max.	45.0	0.50	0.35	Balance	3.10	1.0	1.0	0.03	0.10	0.60	0.03	14.0	7.0	0.02

Incoloy 901 Physical properties:

Density	8.14 g/cm3
Melting point	1280-1345°C

Incoloy 901 minimum mechanical properties in the room temperature:

Status	Tensile strength Rm N/mm2	Yield strength RP0.2N/mm2	Elongation A5 %
Incoloy 901	1034	689	12

Description
A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.

Corrosion Resistance
Alloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.

Workability

Hot Working
Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.

Weldability
Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging